Marble

   Throughout the centuries we find in the whole world grand palaces, temples and structures built out of marble. It is a stone that resists the wear of time and adds greatness wherever it is applied.
   GGM presents you with a collection of the best marbles from Spain, Italy (Carrera), Turkey, Bulgaria and having at the top of the list the Royal White marble of Kozani, originating from Greece, a country world-known for it’s elegant monuments.

ROYAL WHITE KOZANIS

WHITE KOZANI
TEST RESULTS
Absoption coefficient 0.08 wt%
Compressive strength 97.00 MPa
Modulus of rapture 12.90 MPa
Abrasion resistance 2.65 mm
Calcite 98 %
Dolomite 1 %
Quartz 1 %

SEMI WHITE KOZANIS

SEMI WHITE KOZANI
TEST RESULTS
Absoption coefficient 0.08 wt%
Compressive strength 97.00 MPa
Modulus of rapture 12.90 MPa
Abrasion resistance 2.65 mm
Calcite 98 %
Dolomite 1 %
Quartz 1 %

FOUME KOZANIS

FOUME KOZANI
TEST RESULTS
Absorption Coefficient 0.08 wt%
Compressive Strength 97.00 MPa
Modulus Of Rupture 12.90 MPa
Abrasion resistance 2.65 mm
Calcite 98 %
Dolomite 1 %
Quartz 1 %

RODITIS

RODITIS
TEST RESULTS
Absoption coefficient 0.07 wt%
Compressive strength 63.00 MPa
Modulus of rapture 20.00 MPa
Abrasion resistance 2.28 mm
Calcite 97 %
Dolomite 2 %
Quartz 1 %

BRESCIA SINAI

BRESCIA SINAI
TEST (ACCORDING TO ASTM STANDARDS) RESULTS
Abrasion resistance Hardness
[ ASTM C241 / C1353 ]
33.9 Ha
Flexural Strength Mpa
[ ASTM C880 ]
1600 Psi
Modulus Of Rupture Mpa.
[ ASTM C99 ]
2000 Psi
Compressive Strength Mpa.
[ ASTM C170 ]
20200 Psi
Absorbation by Weight
[ ASTM C97 ]
0.26 %
Density
[ ASTM C97 ]
2662 Kg / m3

GALALA

BRESCIA SINAI
TEST (ACCORDING TO ASTM STANDARDS) RESULTS
Abrasion resistance Hardness
[ ASTM C241 / C1353 ]
33.9 Ha
Flexural Strength Mpa
[ ASTM C880 ]
1600 Psi
Modulus Of Rupture Mpa.
[ ASTM C99 ]
2000 Psi
Compressive Strength Mpa.
[ ASTM C170 ]
20200 Psi
Absorbation by Weight
[ ASTM C97 ]
0.26 %
Density
[ ASTM C97 ]
2662 Kg / m3

KHATEMYA

KHATEMYA
TEST (ACCORDING TO ASTM STANDARDS) RESULTS
Abrasion resistance Hardness
[ ASTM C241 / C1353 ]
35.7 Ha
Flexural Strength Mpa
[ ASTM C880 ]
1800 Psi
Modulus Of Rupture Mpa.
[ ASTM C99 ]
2000 Psi
Compressive Strength Mpa.
[ ASTM C170 ]
21300 Psi
Absorbation by Weight
[ ASTM C97 ]
0.87 %
Density
[ ASTM C97 ]
2590 Kg / m3

SAMAHA

SAMAHA
TEST (ACCORDING TO ASTM STANDARDS) RESULTS
Abrasion resistance Hardness
[ ASTM C241 / C1353 ]
35.7 Ha
Flexural Strength Mpa
[ ASTM C880 ]
1800 Psi
Modulus Of Rupture Mpa.
[ ASTM C99 ]
2000 Psi
Compressive Strength Mpa.
[ ASTM C170 ]
21300 Psi
Absorbation by Weight
[ ASTM C97 ]
0.87 %
Density
[ ASTM C97 ]
2590 Kg / m3

SILVIA DARK

SILVIA DARK
TEST (ACCORDING TO ASTM STANDARDS) RESULTS
Abrasion resistance Hardness
[ ASTM C241 / C1353 ]
26.7 Ha
Flexural Strength Mpa
[ ASTM C880 ]
1000 Psi
Modulus Of Rupture Mpa.
[ ASTM C99 ]
1400 Psi
Compressive Strength Mpa.
[ ASTM C170 ]
10400 Psi
Absorbation by Weight
[ ASTM C97 ]
1.62 %
Density
[ ASTM C97 ]
2478 Kg / m3

SILVIA LIGHT

SILVIA LIGHT
TEST (ACCORDING TO ASTM STANDARDS) RESULTS
Abrasion resistance Hardness
[ ASTM C241 / C1353 ]
26.7 Ha
Flexural Strength Mpa
[ ASTM C880 ]
1000 Psi
Modulus Of Rupture Mpa.
[ ASTM C99 ]
1500 Psi
Compressive Strength Mpa.
[ ASTM C170 ]
10400 Psi
Absorbation by Weight
[ ASTM C97 ]
1.62 %
Density
[ ASTM C97 ]
2478 Kg / m3

SUNNY DARK

SUNNY DARK
TEST (ACCORDING TO ASTM STANDARDS) RESULTS
Abrasion resistance Hardness
[ ASTM C241 / C1353 ]
26.4 Ha
Flexural Strength Mpa
[ ASTM C880 ]
1600 Psi
Modulus Of Rupture Mpa.
[ ASTM C99 ]
2000 Psi
Compressive Strength Mpa.
[ ASTM C170 ]
13300 Psi
Absorbation by Weight
[ ASTM C97 ]
0.30 %
Density
[ ASTM C97 ]

SUNNY LIGHT

SUNNY LIGHT
TEST (ACCORDING TO ASTM STANDARDS) RESULTS
Abrasion resistance Hardness
[ ASTM C241 / C1353 ]
26.4 Ha
Flexural Strength Mpa
[ ASTM C880 ]
1600 Psi
Modulus Of Rupture Mpa.
[ ASTM C99 ]
2000 Psi
Compressive Strength Mpa.
[ ASTM C170 ]
13300 Psi
Absorbation by Weight
[ ASTM C97 ]
0.30 %
Density
[ ASTM C97 ]
2618 Kg / m3

TERIESTA

TERIESTA
TEST (ACCORDING TO ASTM STANDARDS) RESULTS
Abrasion resistance Hardness
[ ASTM C241 / C1353 ]
38.8 Ha
Flexural Strength Mpa
[ ASTM C880 ]
1900 Psi
Modulus Of Rupture Mpa.
[ ASTM C99 ]
1900 Psi
Compressive Strength Mpa.
[ ASTM C170 ]
19800 Psi
Absorbation by Weight
[ ASTM C97 ]
0.89 %
Density
[ ASTM C97 ]
2628 Kg / m3

SIVEC WHITE

SIVEC WHITE
TEST RESULTS
Abrasion resistance (after 1000 m) 6.58 mm
Modulus Of Rupture 132 Kg / cm2
Compression Strength 990 Kg / cm2
Absorption Coefficient 0.23 wt%
Apparent Specific Weight 2770 Kg / m3
Microhardness Knoop 321.6 Kg / mm2
Calcite 8 %
Dolomite 90 %
Quartz 2 %

THASSOS WHITE

THASSOS WHITE
TEST RESULTS
Abrasion resistance (after 1000 m) 6.58 mm
Modulus Of Rupture 132 Kg / cm2
Compression Strength 990 Kg / cm2
Absorption Coefficient 0.23 wt%
Apparent Specific Weight 2850 Kg / m3
Microhardness Knoop 321.6 Kg / mm2
Calcite 12 %
Dolomite (%) 86 %
Quartz 2 %

VRATZA

VRATZA
TEST RESULTS
Reaction to fire Class A1
Flexural strength 18.8 MPa
Resistance to fixings 1850 N
Water absorption at atmospheric pressure 5.1 % per mass
Water absorption coefficient by capillarity 15.53 g / (m2 x sec0,5)
Apparent density 2250 kg / m3
Open porosity 16.4 % per volume
Abrasion resistance 19683 mm3 (loss in volume)

CREMA MARFIL

CREMA MARFIL
TEST RESULTS
Compression Strenght 122,84 MPa
Bending Strenght 19,41 MPa
Volumetric Weight 2,72 gm / cm3
Friction Wear Resistance 0,35 mm
Porosity 0,10 %
Knoop Micro-hardness 1774,5 MPa
Absorption Coefficient 0,15 %
Impact Test (minimum height) 42 cms

DARK EMPERADOR

DARK EMPERADOR
TEST RESULTS
Compression Strenght 136,47 MPa
Bending Strenght 25,98 MPa
Volumetric Weight 2,65 gm / cm3
Friction Wear Resistance 0,4 mm
Porosity 1,20 %
Knoop Micro-hardness 1839,21 MPa
Absorption Coefficient 0,40 %
Impact Test (minimum height) 46 cms

DIONYSSOS

DIONYSSOS
TEST RESULTS
Reaction to fire Class A1
Flexural strength 18.9 MPa
Resistance to fixings 1950 N
Compressive strength 91 MPa
Water absorption at atmospheric pressure 0.1 % per mass
Water absorption coefficient by capillarity 0.173 g / (m2 x sec0,5)
Apparent density 2720 kg / m3
Open porosity 0.3 % per volume
Abrasion resistance 21378 mm3 (loss in volume)

LIGHT EMPERADOR

LIGHT EMPERADOR
TEST RESULTS
Hardness 3,5-4 Mohs
Unit Volume Weight 2650 Kg / m3
Density 2680 Kg / m3
Porosity 0,1 %
Water Absorbation 0,35 %
Compressive Strenght 958 Kg / cm2

CARRARA

CARRARA
TEST RESULTS
Absorbtion by weight
(C97)
0.11 %
Density
(C97)
169.73 lbs/ft3
Compressive strenght
(C170)
12,972 psi
Abrasion resist. Hardness
(C241)
15.04
Flexural strength
(C880)
697 psi

KOKY BEIGE

KOKY BEIGE

SANDWAVE

SANDWAVE

ADONIS PEARL

ADONIS PEARL

ADONIS ROSE

ADONIS ROSE

CAPPUCINO

CAPPUCINO

LIMESTONE

LIMESTONE